Absorbable Surgical sutures
Products
Information
DAMACRYL
Polymer Structure: 100% Poly Glycolic Acid (PGA)
Filament Type: Multifilament
Coating: Polycaprolactone and calcium stearate
USP Range: 10/0 to 3
Tensile Strength: More than 65% of the initial strength after 14 days at 37°C
Absorption Period: Completely absorbed in 60-90 days
Sterilization: Ethylene Oxide
Color: Violet, Undyed
Shelf Life: 5 years
Moisture content: Below 400ppm
Features:
• Predictable absorption
• In-vivo inertness (less reactive)
• Excellent knot security
• Easy handling properties
DAMACRYL 910
Polymer Structure: Poly (glycolide-co- L- lactide) (90/10) / Polyglactin-910
Filament Type: Multifilament
Coating: Poly (glycolide-co- -lactide) (30/70) and Calcium stearate
USP Range: 8/0 to 3
Tensile Strength: More than 65% of the initial strength after 14 days at 37°C
Absorption Period: Completely absorbed in 54-70 days
Sterilization: EO
Color: Violet, Undyed
Shelf Life: 5 years
Moisture content: Below 400ppm
Features:
• predictable absorption
• in-vivo inertness (less reactive)
• excellent knot security
• easy handling properties
DAMACRYL Rapid
Polymer Structure: Poly (glycolide-co- L- lactide) (90/10) / Polyglactin-910
Filament Type: Multifilament
Coating: Poly (glycolide-co- -lactide) (30/70) and Calcium stearate
USP Range: 6/0 to 2
Tensile Strength: About 50% of the initial strength after 7 days at 37°C
Absorption Period: Completely absorbed in 40-60 days / FAST-term Absorbable
Sterilization: EO
Color: Undyed
Shelf Life: 3 years
Moisture Content: Below 400ppm
Features:
• Fast absorption
• In-vivo inertness (less reactive)
• Excellent knot security
• Easy handling properties
DAMADIOXANONE
Structure: 100% homo polymer of Poly (p-dioxanone) (PDO)
Filament Type: Monofilament
Coating: None
USP Range: 7/0 to 2
Tensile Strength: about 65% of the initial strength after 4 Weeks at 37°C
Absorption Period: Completely absorbed in 180-240 days
Sterilization: EO
Color: Violet
Shelf Life: 3 years
Moisture Content: Below 400ppm
Features:
• Long Term W